Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials

Çiğdem Büyükkök, Arife Kaptan

Purpose To evaluate the temperature changes in primary teeth pulp chambers of different dentin thicknesses during polymerization of four glass ionomer-based restorative materials. Materials and Methods Eighty extracted, caries-free, primary molars were prepared as standardized Class I occlusal cavities with dentin thicknesses of 1 mm and 2 mm. Four glass ionomerbased restorative materials, Dyract XP, Photac Fil Quick Aplicap, Fuji II LC, and GCP Glass Fill, were placed in the cavities and cured with two light-curing units. Temperature increases (initial temperature, 37°C) in the pulp chamber during polymerization were recorded by a J-type thermocouple in a pulpal microcirculation set-up. The data were analyzed with Variance analyses and Tukey tests. Results The temperatures recorded in samples with dentin thicknesses of 1 mm and 2 mm exhibited statistically significant differences (p<0.05). The GCP Glass Fill group exhibited the highest temperature increases for both dentin thicknesses (p<0.05). The other groups were not statistically different but the Dyract XP group exhibited the least temperature change. Conclusion The highest temperature changes were observed for 1 mm dentin thickness. All temperature increases during polymerizations and setting reactions were lower than the corresponding critical values 5.5°C.

Keywords: Glass carbomer, Glass ionomer, Primary teeth, Temperature increase, Pulp

PDF View

References

  • 1. Öztürk B, Üşümez A, Öztürk AN, Ozer F. In vitro assessment of temperature change in the pulp chamber during cavity preparation. J Prosthet Dent 2004;91:436-40. [CrossRef] google scholar
  • 2. Schneider L, Consani S, Correr-Sobrinho L, Correr A, Sinhoreti M. Halogen and LED light curing of composite: Temperature increase and Knoop hardness. Clin Oral Investig 2006;10:66-71. [CrossRef] google scholar
  • 3. Al-Qudah A, Mitchell C, Biagioni P, Hussey D. Effect of composite shade, increment thickness and curing light on temperature rise during photocuring. J Dent 2007;35:238-45. [CrossRef] google scholar
  • 4. Zach L, Cohen G. Pulp response to externally applied heat. Oral Surg Oral Med Oral Pathol 1965;19:515-30. [CrossRef] google scholar
  • 5. Agematsu H, Abe S, Shiozaki K, Usami A, Ogata S, Suzuki K, Soejima M, Ohnishi M, Nonami K, Ide Y. Relationship between large tubules and dentin caries in human deciduous tooth. Bull Tokyo Dent Coll 2005;46:7-15. [CrossRef] google scholar
  • 6. Paghdiwala A, Vaidyanathan T, Paghdiwala M. Evaluation of erbium: YAG laser radiation of hard dental tissues: Analysis of temperature changes, depth of cuts and structural effects. Scanning microsc 1993;7:989-97. google scholar
  • 7. Maruo IT, Godoy-Bezerra J, Saga AY, Tanaka OM, Maruo H, Camargo ES. Effect of etching and light-curing time on the shear bond strength of a resin-modified glass ionomer cement. Brazilian dental journal 2010;21:533-7. [CrossRef] google scholar
  • 8. Fajen VB, Duncanson MG, Jr., Nanda RS, Currier GF, Angolkar PV. An in vitro evaluation of bond strength of three glass ionomer cements. American journal of orthodontics and dentofacial orthopedics : official publication of the American Association of Orthodontists, its constituent societies, and the American Board of Orthodontics 1990;97:316-22. [CrossRef] google scholar
  • 9. Pereira LC, Nunes MC, Dibb RG, Powers JM, Roulet JF, Navarro MF. Mechanical properties and bond strength of glass-ionomer cements. The journal of adhesive dentistry 2002;4:73-80. google scholar
  • 10. Horváth A, Papp Z, Dobó-Nagy C, Gera I. Clinical examination of the gingival effects of three glass ionomer restorative materials (GC fuji IX GP, GC fuji IX GP EXTRA és GC EQUIA). Fogorvosi szemle 2014;107:125-30. google scholar
  • 11. Koenraads H, Van der Kroon G, Frencken J. Compressive strength of two newly developed glass-ionomer materials for use with the Atraumatic Restorative Treatment (ART) approach in class II cavities. Dent Mater 2009;25:551-6. [CrossRef] google scholar
  • 12. Menne-Happ U, Ilie N. Effect of gloss and heat on the mechanical behaviour of a glass carbomer cement. J Dent 2013;41:223-30. [CrossRef] google scholar
  • 13. Savas S, Botsali MS, Kucukyilmaz E, Sari T. Evaluation of temperature changes in the pulp chamber during polymerization of light-cured pulp-capping materials by using a VALO LED light curing unit at different curing distances. Dent Mater 2014;33:764-9. [CrossRef] google scholar
  • 14. Gavic L, Gorseta K, Glavina D, Czarnecka B, Nicholson JW. Heat transfer properties and thermal cure of glass-ionomer dental cements. J Mater Sci Mater Med 2015;26:249. [CrossRef] google scholar
  • 15. Al-Qudah A, Mitchell C, Biagioni P, Hussey D. Thermographic investigation of contemporary resin-containing dental materials. J Dent 2005;33:593-602. [CrossRef] google scholar
  • 16. Ozturk B, Ozturk A, Usumez A, Usumez S, Ozer F. Temperature rise during adhesive and resin composite polymerization with various light curing sources. Oper Dent 2004;29:325-32. google scholar
  • 17. Koutsi V, Noonan R, Horner J, Simpson M, Matthews W, Pashley DH. The effect of dentin depth on the permeability and ultrastructure of primary molars. Pediatr Dent 1994;16:29-35. google scholar
  • 18. Mjör P. Dentin-predentin complex and its permeability: Pathology and treatment overview. J Dent Res 1985;64:621-7. [CrossRef] google scholar
  • 19. Guiraldo RD, Consani S, Lympius T, Schneider LF, Sinhoreti MA, Correr-Sobrinho L. Influence of the light curing unit and thickness of residual dentin on generation of heat during composite photoactivation. J Oral Sci 2008;50:137-42. [CrossRef] google scholar
  • 20. Ramoglu SI, Karamehmetoglu H, Sari T, Usumez S. Temperature rise caused in the pulp chamber under simulated intrapulpal microcirculation with different light-curing modes. Angle Orthod 2015;85:381-5. [CrossRef] google scholar
  • 21. Kodonas K, Gogos C, Tziafas D. Effect of simulated pulpal microcirculation on intrapulpal temperature changes following application of heat on tooth surfaces. Int Endod J 2009;42:247- 52. [CrossRef] google scholar
  • 22. Michalakis K, Pissiotis A, Hirayama H, Kang K, Kafantaris N. Comparison of temperature increase in the pulp chamber during the polymerization of materials used for the direct fabrication of provisional restorations. J Prosthet Dent 2006;96:418-23. [CrossRef] google scholar
  • 23. Kodonas K, Gogos C, Tziafa C. Effect of simulated pulpal microcirculation on intrachamber temperature changes following application of various curing units on tooth surface. J Dent 2009;37:485-90. [CrossRef] google scholar
  • 24. Carrasco TG, Carrasco-Guerisoli LD, Fröner IC. In vitro study of the pulp chamber temperature rise during light-activated bleaching. J Appl Oral Sci 2008;16:355-9. [CrossRef] google scholar
  • 25. Altan H, Göztas Z, Arslanoglu Z. Bulk-Fill restorative materials in primary tooth: An intrapulpal temperature changes study. Contemp Clin Dent 2018;9:52-7. [CrossRef] google scholar
  • 26. Botsali MS, Tokay U, Ozmen B, Cortcu M, Koyuturk AE, Kahvecioglu F. Effect of new innovative restorative carbomised glass cement on intrapulpal temperature rise: an ex-vivo study. Braz Oral Res 2016;30. [CrossRef] google scholar
  • 27. Loney R, Price R. Temperature transmission of high-output lightcuring units through dentin. Oper Dent 2001;26:516-20. google scholar
  • 28. Takahashi N, Kitagami T, Komori T. Evaluation of thermal change in pulp chamber. J Dent Res 1977;56:1480. [CrossRef] google scholar
  • 29. Hubbezoglu I, Dogan A, Dogan O, Demir H. Kompozit rezin materyallerin farkli ışık kaynaklarıyla polimerizasyonu sırasında oluşan ısısal değişikliklerin incelenmesi. Cumhuriyet Dent J 2008;11:16-22. google scholar
  • 30. Baroudi K, Silikas N, Watts DC. In vitro pulp chamber temperature rise from irradiation and exotherm of flowable composites. Int J Paediatr Dent 2009;19:48-54. [CrossRef] google scholar
  • 31. Müjdeci A, Yeşilyurt A, Gökay O. Kompozit rezinlerin polimerizasyonları esnasında pulpa odasındaki ısı değişimlerinin in vitro değerlendirilmesi. AÜ Diş Hek Fak Derg 2005;32:163-9. [CrossRef] google scholar
  • 32. Kahvecioglu F, Tosun G, Ülker HE. Intrapulpal thermal changes during setting reaction of glass Carbomer® using thermocure lamp. Biomed Res Int 2016:1-7. [CrossRef] google scholar

Citations

Copy and paste a formatted citation or use one of the options to export in your chosen format


EXPORT



APA

Büyükkök, Ç., & Kaptan, A. (2021). Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials. European Oral Research, 55(1), 28-33. https://doi.org/10.26650/eor.20210024


AMA

Büyükkök Ç, Kaptan A. Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials. European Oral Research. 2021;55(1):28-33. https://doi.org/10.26650/eor.20210024


ABNT

Büyükkök, Ç.; Kaptan, A. Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials. European Oral Research, [Publisher Location], v. 55, n. 1, p. 28-33, 2021.


Chicago: Author-Date Style

Büyükkök, Çiğdem, and Arife Kaptan. 2021. “Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials.” European Oral Research 55, no. 1: 28-33. https://doi.org/10.26650/eor.20210024


Chicago: Humanities Style

Büyükkök, Çiğdem, and Arife Kaptan. “Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials.” European Oral Research 55, no. 1 (Apr. 2024): 28-33. https://doi.org/10.26650/eor.20210024


Harvard: Australian Style

Büyükkök, Ç & Kaptan, A 2021, 'Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials', European Oral Research, vol. 55, no. 1, pp. 28-33, viewed 24 Apr. 2024, https://doi.org/10.26650/eor.20210024


Harvard: Author-Date Style

Büyükkök, Ç. and Kaptan, A. (2021) ‘Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials’, European Oral Research, 55(1), pp. 28-33. https://doi.org/10.26650/eor.20210024 (24 Apr. 2024).


MLA

Büyükkök, Çiğdem, and Arife Kaptan. “Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials.” European Oral Research, vol. 55, no. 1, 2021, pp. 28-33. [Database Container], https://doi.org/10.26650/eor.20210024


Vancouver

Büyükkök Ç, Kaptan A. Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials. European Oral Research [Internet]. 24 Apr. 2024 [cited 24 Apr. 2024];55(1):28-33. Available from: https://doi.org/10.26650/eor.20210024 doi: 10.26650/eor.20210024


ISNAD

Büyükkök, Çiğdem - Kaptan, Arife. “Temperature increases in primary teeth pulp chamber during polymerization of glass ionomer-based restorative materials”. European Oral Research 55/1 (Apr. 2024): 28-33. https://doi.org/10.26650/eor.20210024



TIMELINE


Submitted12.03.2020
Accepted07.10.2020
Published Online31.01.2021

LICENCE


Attribution-NonCommercial (CC BY-NC)

This license lets others remix, tweak, and build upon your work non-commercially, and although their new works must also acknowledge you and be non-commercial, they don’t have to license their derivative works on the same terms.


SHARE




Istanbul University Press aims to contribute to the dissemination of ever growing scientific knowledge through publication of high quality scientific journals and books in accordance with the international publishing standards and ethics. Istanbul University Press follows an open access, non-commercial, scholarly publishing.